Flexible packaging material

ABSTRACT

Described herein is a process for preparing a flexible packaging material (6). The process may comprise: providing a base material (1) having a first surface (1a) and a second surface (1b), the first surface (1a) having an electrostatic ink composition (4) printed thereon; providing a sealant layer (3) on the second surface (1b) of the base material (1); providing a flexible substrate (4) on which a thermally activatable laminating layer (5) has been deposited; and contacting under conditions of heat and/or pressure the thermally activatable laminating layer (5) disposed on the flexible substrate (4) with the first surface (1a) of the base material (1) on which the electrostatic ink composition (4) is printed.

BACKGROUND

All manner of consumer goods, in particular food products, are packaged using thin films or sheets of flexible packaging material, with images such as corporate branding, or product information printed onto the film. The flexible packaging material serves to protect the product from, for example, moisture, oxidation or pathogens, while also providing information to the user regarding the nature and origin of the product contained therein.

Liquid electrophotographic printing, or electrostatic printing, is one method by which images or information can be printed onto substrates such as paper or plastic. The printing processes generally involve creating an image on a photoconductive surface, applying an ink having charged particles to the photoconductive surface, such that they selectively bind to the image, and then transferring the charged particles in the form of the image to a print substrate.

BRIEF DESCRIPTION OF THE FIGURE

FIG. 1 shows a schematic process for producing a flexible packaging material.

DETAILED DESCRIPTION

Before the present disclosure is disclosed and described, it is to be understood that this disclosure is not limited to the particular process features and materials disclosed herein because such process features and materials may vary somewhat. It is also to be understood that the terminology used herein is used for the purpose of describing particular examples.

It is noted that, as used in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise.

As used herein, “carrier fluid”, “carrier liquid,” “carrier,” or “carrier vehicle” refers to the fluid in which pigment particles, colorant, charge directors and other additives can be dispersed to form a liquid electrostatic composition or electrophotographic composition. The carrier liquids may include a mixture of a variety of different agents, such as surfactants, co-solvents, viscosity modifiers, and/or other possible ingredients.

As used herein, “electrostatic ink composition” or “liquid electrophotographic composition” generally refers to an ink composition that is generally suitable for use in an electrostatic printing process, sometimes termed an electrophotographic printing process. It may comprise pigment particles, which may comprise a thermoplastic resin.

As used herein, “pigment” generally includes pigment colorants, magnetic particles, aluminas, silicas, and/or other ceramics or organo-metallics, whether or not such particulates impart color. Thus, though the present description primarily exemplifies the use of pigment colorants, the term “pigment” can be used more generally to describe not just pigment colorants, but other pigments such as organometallics, ferrites, ceramics, etc.

As used herein, “co-polymer” refers to a polymer that is polymerized from at least two monomers.

As used herein, “lamination bond strength” refers to the force (per length) required to delaminate a laminated material, and is expressed in units of Newton/inch, or N/in. The lamination bond strength can be measured according to standard techniques, in particular ASTM F0904-98R08. Unless otherwise stated, the lamination bond strength of a flexible packaging material described herein refers the strength to delaminate the material at the interface between a thermally activatable laminating material and either of the two materials to which the thermally activatable laminating material has bonded.

As used herein, “melt flow rate” generally refers to the extrusion rate of a resin through an orifice of defined dimensions at a specified temperature and load, usually reported as temperature/load, e.g. 190° C./2.16 kg. Flow rates can be used to differentiate grades or provide a measure of degradation of a material as a result of molding. In the present disclosure, “melt flow rate” is measured per ASTM D1238-04c Standard Test Method for Melt Flow Rates of Thermoplastics by Extrusion Plastometer. If a melt flow rate of a particular polymer is specified, unless otherwise stated, it is the melt flow rate for that polymer alone, in the absence of any of the other components of the electrostatic composition.

As used herein, “acidity,” “acid number,” or “acid value” refers to the mass of potassium hydroxide (KOH) in milligrams that neutralizes one gram of a substance. The acidity of a polymer can be measured according to standard techniques, for example as described in ASTM D1386. If the acidity of a particular polymer is specified, unless otherwise stated, it is the acidity for that polymer alone, in the absence of any of the other components of the liquid toner composition.

As used herein, “melt viscosity” generally refers to the ratio of shear stress to shear rate at a given shear stress or shear rate. Testing is generally performed using a capillary rheometer. A plastic charge is heated in the rheometer barrel and is forced through a die with a plunger. The plunger is pushed either by a constant force or at constant rate depending on the equipment. Measurements are taken once the system has reached steady-state operation. One method used is measuring Brookfield viscosity @ 140° C., units are mPa-s or cPoise. In some examples, the melt viscosity can be measured using a rheometer, e.g. a commercially available AR-2000 Rheometer from Thermal Analysis Instruments, using the geometry of: 25 mm steel plate-standard steel parallel plate, and finding the plate over plate rheometry isotherm at 120° C., 0.01 hz shear rate. If the melt viscosity of a particular polymer is specified, unless otherwise stated, it is the melt viscosity for that polymer alone, in the absence of any of the other components of the electrostatic composition.

In some examples, the melting point of a resin or polymer described herein may be the melting point measured according to ASTM D3418.

A certain monomer may be described herein as constituting a certain weight percentage of a polymer. This indicates that the repeating units formed from the said monomer in the polymer constitute said weight percentage of the polymer.

If a standard test is mentioned herein, unless otherwise stated, the version of the test to be referred to is the most recent at the time of filing this patent application.

As used herein, “electrostatic printing” or “electrophotographic printing” generally refers to the process that provides an image that is transferred from a photo imaging substrate either directly or indirectly via an intermediate transfer member to a print substrate. As such, the image is not substantially absorbed into the photo imaging substrate on which it is applied. Additionally, “electrophotographic printers” or “electrostatic printers” generally refer to those printers capable of performing electrophotographic printing or electrostatic printing, as described above. “Liquid electrophotographic printing” is a specific type of electrophotographic printing where a liquid composition is employed in the electrophotographic process rather than a powder toner. An electrostatic printing process may involve subjecting the electrostatic composition to an electric field, e.g. an electric field having a field gradient of 50-400V/μm, or more, ins some examples 600-900V/μm, or more.

As used herein, the term “about” is used to provide flexibility to a numerical range endpoint by providing that a given value may be a little above or a little below the endpoint to allow for variation in test methods or apparatus. The degree of flexibility of this term can be dictated by the particular variable.

As used herein, a plurality of items, structural elements, compositional elements, and/or materials may be presented in a common list for convenience. However, these lists should be construed as though each member of the list is individually identified as a separate and unique member. Thus, no individual member of such list should be construed as a de facto equivalent of any other member of the same list solely based on their presentation in a common group without indications to the contrary.

Concentrations, amounts, and other numerical data may be expressed or presented herein in a range format. It is to be understood that such a range format is used merely for convenience and brevity and thus should be interpreted flexibly to include not just the numerical values explicitly recited as the end points of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. As an illustration, a numerical range of “about 1 wt % to about 5 wt %” should be interpreted to include not just the explicitly recited values of about 1 wt % to about 5 wt %, but also include individual values and subranges within the indicated range. Thus, included in this numerical range are individual values such as 2, 3.5, and 4 and sub-ranges such as from 1-3, from 2-4, and from 3-5, etc. This same principle applies to ranges reciting a single numerical value. Furthermore, such an interpretation should apply regardless of the breadth of the range or the characteristics being described.

As used herein, wt % values are to be taken as referring to a weight-for-weight (w/w) percentage of solids in the ink composition, and not including the weight of any carrier fluid present.

Unless otherwise stated, any feature described herein can be combined with any aspect or any other feature described herein.

In an aspect there is provided a process for preparing a flexible packaging material. The process for preparing a flexible packaging material may comprise:

-   -   providing a base material having a first surface and a second         surface, the first surface having an electrostatic ink         composition printed thereon;     -   providing a sealant layer on the second surface of the base         material;     -   providing a flexible substrate on which a thermally activatable         laminating layer has been deposited; and

contacting under conditions of heat and/or pressure the thermally activatable laminating layer disposed on the flexible substrate with the first surface of the base material on which the electrostatic ink composition is printed.

In another aspect there is provided a flexible packaging material. The flexible packaging material may comprise:

-   -   a base material comprising a first surface and a second surface;     -   an electrostatic ink composition printed on the first surface of         the base material;     -   a sealant layer disposed on the second surface of the base         material;     -   a flexible substrate; and         -   a thermally activated laminating layer disposed between and             bonded to the flexible substrate and the first surface of             the base material printed with the electrostatic ink             composition.

In another aspect there is provided a flexible package. The flexible package may comprise a flexible material comprising:

-   -   a base material comprising a first surface and a second surface;     -   an electrophotographic ink composition printed on the first         surface of the base material;     -   a sealant layer disposed on the second surface of the base         material;

a flexible substrate; and

-   -   a thermally activated laminating layer disposed between and         bonded to the flexible substrate and the first surface of the         base material printed with the ink composition.

Much research has been carried out in recent years to try to develop laminated flexible packaging materials comprising a functional (barrier) substrate laminated to a second substrate comprising a printed image or information. Many solvent based or even “solvent free” laminating adhesives require a prolonged period of curing, and so there is a lag time between a flexible packaging material being produced and the material being ready for packaging food. Thus, when used with digital printing processes, existing laminating technologies may negate the advantage of short turnaround on the printing process due to long post-printing processes/wait times.

The present inventors have found that examples of the method as described herein avoid or at least mitigate at least one of the difficulties described above. They have found that examples of the method are more successful than previous methods in that the lamination and bonding is immediate such that no cure time is required. The methods described can be implemented in-line with an existing electrostatic printing process, thus further streamlining the process for producing flexible packaging materials.

The present inventors have also found that examples of the method as described herein provide a more cost efficient process and/or a process in which less storage space for materials is required compared to some existing processes.

Flexible Packaging Material

In some examples, a flexible packaging material is described. The flexible packaging material may be produced by any of the methods described herein. Each component of the flexible packaging material will be discussed in the sections which follow.

In some examples, the flexible packaging material comprises a laminate structure with sufficient bond strength to avoid delamination of the layers, in particular delamination at the interface between the layer of laminating material (which may be thermally activatable) and the surface of the print substrate comprising the electrophotographically printed image or information. In some examples, the lamination bond strength is measured directly after the flexible packaging material has cooled to room temperature following lamination. In some examples, the lamination bond strength is measured on a flexible packaging material that has not been subjected to any curing or rest period following lamination and cooling. In some examples, the lamination bond strength is measured immediately after lamination and cooling of the flexible packaging material.

In some examples, the flexible packaging material has a lamination bond strength as measured by ASTM F0904-98R08. In some examples, the flexible packaging material has a lamination bond strength of at least about 0.5 N/inch, for example at least about 1.0 N/inch, for example at least about 1.2 N/inch, for example at least about 1.5 N/inch, for example at least about 2.0 N/inch, for example at least about 2.5 N/inch, for example at least about 3.0 N/inch, for example at least about 4.0 N/inch, for example at least about 5.0 N/inch, for example at least about 6.0 N/inch, for example at least about 7.0 N/inch, for example at least about 8.0 N/inch, for example at least about 9.0 N/inch, for example about 10.0 N/inch, as measured by ASTM F0904-98R08.

In some examples, the flexible packaging material has a lamination bond strength of between about 2 N/inch to about 10 N/inch.

Base Material (Print Substrate)

The base material, to which a liquid electrostatic ink composition may be printed (and thus is also referred to herein as the print substrate) may be any material suitable for use in a liquid electrophotographic printing process and suitable for use in a flexible packaging material. In some examples, the base material is a flexible base material.

The base material of the flexible packaging material may also be referred to as a functional substrate or simply a base layer. The base layer of the flexible packaging material may be the innermost layer of the flexible packaging material in use, and may thus be in contact with the packaged goods. In some examples the base layer is referred to as a functional substrate and is functional in the sense that it provides a barrier function to protect the packaged goods. The base layer or functional substrate may serve as a barrier to any external influence that could damage or otherwise reduce the quality of the packaged goods, in particular food, by preventing ingress of, for example, moisture, oxygen, other oxidants and pathogens such as viruses and bacteria.

In some examples, the base material comprises a film or sheet, e.g. a thin film or thin sheet, of paper, metallic foil, and/or plastic. In some examples, the base material comprises a metallic foil, a metallized substrate or a paper substrate. In some examples, the base material comprises a metallic foil or a metallized substrate. In some examples, the base material comprises a paper substrate. In some examples, the base material comprises a metallized paper or a metallized plastic film. In some examples, the base material comprises an aluminium foil. In some examples the base material comprises a film, e.g. a thin film, of a plastic material, for example, polyethylene (PE), linear low density polyethylene (LLDPE), low density polyethylene (LDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), polypropylene (PP), biaxially oriented polypropylene (BOPP), oriented polyamide (OPA). In some examples, the base material comprises a plurality of layers of film of a plastic material, such as a combination of films selected from PE, LLDPE, PP, BOPP and OPA, laminated together.

In some examples, the base material comprises a metallized paper in the form of a paper substrate coated on one surface with a layer of metal, for example aluminium.

In some examples, the base material comprises a metallized plastic film in the form of a polymer substrate coated on one surface with a layer of metal, for example aluminium. In some examples, the base material comprises a metallized plastic film in the form of a metallized BOPP film, a metallized PET film. In some examples, an aluminium layer is 7-12 μm in thickness and is laminated to a PE layer.

In some examples, the base layer comprises a thin film of material, wherein the film is less than 100 μm in thickness, for example less than 90 μm in thickness, less than 80 μm in thickness, less than 70 μm in thickness, less than 60 μm in thickness, less than 50 μm in thickness, less than 40 μm in thickness, less than 30 μm in thickness, less than 20 μm in thickness, less than 15 μm in thickness. In some examples, the film of material is about 12 μm in thickness.

In some examples, the base layer comprises a thin film of material, wherein the film is greater than 12 μm in thickness, for example greater than 15 μm in thickness, greater than 20 μm in thickness, greater than 30 μm in thickness, greater than 40 μm in thickness, greater than 50 μm in thickness, greater than 60 μm in thickness, greater than 70 μm in thickness, greater than 80 μm in thickness, greater than 90 μm in thickness. In some examples, the film of material is about 100 μm in thickness.

In some examples, the base material comprises an image or information printed on a first surface of the base material in a liquid electrophotographic printing process using a liquid electrophotographic composition as described herein. The polymer resin of the printed composition may thus be available for thermally laminating the base material (functional substrate) to the flexible substrate described below.

Electrostatic Ink Composition

The electrostatic ink composition printed on a first surface of the base material described herein may be a liquid electrophotographic printing composition (also referred to herein as a LEP composition) printed on the base material using a liquid electrophotographic printing process. The LEP composition may comprise a colorant or pigment, a polymer resin and a carrier fluid or liquid. The LEP composition may further comprise an additive such as a charge director, charge adjuvant, surfactant, viscosity modifier, emulsifier and the like, or combinations thereof. In some examples, the LEP composition may not contain any pigment, or comprise substantially zero pigment and thus be a pigment-free composition, useful in providing a particular transparent gloss or sheen to a printed substrate.

After printing, the electrostatic ink composition printed on the base material may comprise a reduced amount of carrier liquid compared with the LEP printing composition before printing. In some examples, the electrostatic ink composition printed on the base material may be substantially free from carrier liquid. Substantially free from carrier liquid may indicate that the ink printed on the print substrate contains less than 5 wt % carrier liquid, in some examples, less than 2 wt % carrier liquid, in some examples less than 1 wt % carrier liquid, in some examples less than 0.5 wt % carrier liquid. In some examples, the electrostatic ink composition printed on the base material is free from carrier liquid.

Each of these components will be described separately in the sub-sections which follow.

Colorant

The electrostatic ink composition may comprise a colorant. The colorant may be a dye or pigment. The colorant can be any colorant compatible with the liquid carrier and useful for electrophotographic printing. For example, the colorant may be present as pigment particles, or may comprise a resin (in addition to the polymers described herein) and a pigment. The resins and pigments can be any of those standardly used in the art. In some examples, the colorant is selected from a cyan pigment, a magenta pigment, a yellow pigment and a black pigment. For example, pigments by Hoechst including Permanent Yellow DHG, Permanent Yellow GR, Permanent Yellow G, Permanent Yellow NCG-71, Permanent Yellow GG, Hansa Yellow RA, Hansa Brilliant Yellow 5GX-02, Hansa Yellow X, NOVAPERM® YELLOW HR, NOVAPERM® YELLOW FGL, Hansa Brilliant Yellow 10GX, Permanent Yellow G3R-01, HOSTAPERM® YELLOW H4G, HOSTAPERM® YELLOW H3G, HOSTAPERM® ORANGE GR, HOSTAPERM® SCARLET GO, Permanent Rubine F6B; pigments by Sun Chemical including L74-1357 Yellow, L75-1331 Yellow, L75-2337 Yellow; pigments by Heubach including DALAMAR® YELLOW YT-858-D; pigments by Ciba-Geigy including CROMOPHTHAL® YELLOW 3 G, CROMOPHTHAL® YELLOW GR, CROMOPHTHAL® YELLOW 8 G, IRGAZINE® YELLOW SGT, IRGALITE® RUBINE 4BL, MONASTRAL® MAGENTA, MONASTRAL® SCARLET, MONASTRAL® VIOLET, MONASTRAL® RED, MONASTRAL® VIOLET; pigments by BASF including LUMOGEN® LIGHT YELLOW, PALIOGEN® ORANGE, HELIOGEN® BLUE L 690 IF, HELIOGEN® BLUE TBD 7010, HELIOGEN® BLUE K 7090, HELIOGEN® BLUE L 710 IF, HELIOGEN® BLUE L 6470, HELIOGEN® GREEN K 8683, HELIOGEN® GREEN L 9140; pigments by Mobay including QUINDO® MAGENTA, INDOFAST® BRILLIANT SCARLET, QUINDO® RED 6700, QUINDO® RED 6713, INDOFAST® VIOLET; pigments by Cabot including Maroon B STERLING® NS BLACK, STERLING® NSX 76, MOGUL® L; pigments by DuPont including TIPURE® R-101; and pigments by Paul Uhlich including UHLICH® BK 8200.

In some examples, the colorant or pigment particles may have a median particle size or d₅₀ of less than 20 μm, for example less than 15 μm, for example less than 10 μm, for example less than 5 μm, for example less than 4 μm, for example less than 3 μm, for example less than 2 μm, for example less than 1 μm, for example less than 0.9 μm, for example less than 08 μm, for example less than 0.7 μm, for example less than 0.6 μm, for example less than 0.5 μm. Unless otherwise stated, the particle size of the colorant or pigment particle and the resin coated pigment particle is determined using laser diffraction on a Malvern Mastersizer 2000 according to the standard procedure as described in the operating manual.

The colorant or pigment particle may be present in the method and/or electrostatic ink composition in an amount of from 10 wt % to 80 wt % of the total amount of resin and pigment, in some examples 15 wt % to 80 wt %, in some examples 15 wt % to 60 wt %, in some examples 15 wt % to 50 wt %, in some examples 15 wt % to 40 wt %, in some examples 15 wt % to 30 wt % of the total amount of resin and colorant. In some examples, the colorant or pigment particle may be present in the method and/or electrostatic ink composition in an amount of at least 50 wt % of the total amount of resin and colorant or pigment, for example at least 55 wt % of the total amount of resin and colorant or pigment.

Polymer Resin

In some examples, the electrostatic ink composition comprises a polymer resin comprising a copolymer of an alkylene monomer and a monomer selected from acrylic acid and methacrylic acid. The polymer resin may be referred to as a thermoplastic polymer. A thermoplastic polymer is sometimes referred to as a thermoplastic resin. In some examples, the polymer may comprise ethylene or propylene acrylic acid co-polymers; ethylene or propylene methacrylic acid co-polymers; ethylene vinyl acetate co-polymers; co-polymers of ethylene or propylene (e.g. 80 wt % to 99.9 wt %), and alkyl (e.g. C1 to C5) ester of methacrylic or acrylic acid (e.g. 0.1 wt % to 20 wt %); co-polymers of ethylene (e.g. 80 wt % to 99.9 wt %), acrylic or methacrylic acid (e.g. 0.1 wt % to 20.0 wt %) and alkyl (e.g. C1 to C5) ester of methacrylic or acrylic acid (e.g. 0.1 wt % to 20 wt %); co-polymers of ethylene or propylene (e.g. 70 wt % to 99.9 wt %) and maleic anhydride (e.g. 0.1 wt % to 30 wt %); polyethylene; polystyrene; isotactic polypropylene (crystalline); co-polymers of ethylene ethylene ethyl acrylate; polyesters; polyvinyl toluene; polyamides; styrene/butadiene co-polymers; epoxy resins; acrylic resins (e.g. co-polymer of acrylic or methacrylic acid and at least one alkyl ester of acrylic or methacrylic acid wherein alkyl may have from 1 to about 20 carbon atoms, such as methyl methacrylate (e.g. 50% to 90%)/methacrylic acid (e.g. 0 wt % to 20 wt %)/ethylhexylacrylate (e.g. 10 wt % to 50 wt %)); ethylene-acrylate terpolymers:ethylene-acrylic esters-maleic anhydride (MAH) or glycidyl methacrylate (GMA) terpolymers; ethylene-acrylic acid ionomers or combinations thereof.

In some examples, the polymer resin comprises a polymer having acidic side groups. In some examples, the polymer having acidic side groups may have an acidity of 50 mg KOH/g or more, in some examples an acidity of 60 mg KOH/g or more, in some examples an acidity of 70 mg KOH/g or more, in some examples an acidity of 80 mg KOH/g or more, in some examples an acidity of 90 mg KOH/g or more, in some examples an acidity of 100 mg KOH/g or more, in some examples an acidity of 105 mg KOH/g or more, in some examples 110 mg KOH/g or more, in some examples 115 mg KOH/g or more. In some examples, the polymer having acidic side groups may have an acidity of 200 mg KOH/g or less, in some examples 190 mg or less, in some examples 180 mg or less, in some examples 130 mg KOH/g or less, in some examples 120 mg KOH/g or less. Acidity of a polymer, as measured in mg KOH/g can be measured using standard procedures, for example using the procedure described in ASTM D1386.

The resin may comprise a polymer having acidic side groups, that has a melt flow rate of less than about 70 g/10 minutes, in some examples about 60 g/10 minutes or less, in some examples about 50 g/10 minutes or less, in some examples about 40 g/10 minutes or less, in some examples 30 g/10 minutes or less, in some examples 20 g/10 minutes or less, in some examples 10 g/10 minutes or less. In some examples, all polymers having acidic side groups and/or ester groups in the particles each individually have a melt flow rate of less than 90 g/10 minutes, 80 g/10 minutes or less, in some examples 80 g/10 minutes or less, in some examples 70 g/10 minutes or less, in some examples 70 g/10 minutes or less, in some examples 60 g/10 minutes or less.

In some examples, the polymer having acidic side groups may have a melt flow rate of about 10 g/10 minutes to about 120 g/10 minutes, in some examples about 10 g/10 minutes to about 70 g/10 minutes, in some examples about 10 g/10 minutes to 40 g/10 minutes, in some examples 20 g/10 minutes to 30 g/10 minutes. In some examples, the polymer having acidic side groups can have a melt flow rate of, in some examples, about 50 g/10 minutes to about 120 g/10 minutes, in some examples 60 g/10 minutes to about 100 g/10 minutes. The melt flow rate can be measured using standard procedures, for example as described in ASTM D1238.

In some examples, the acidic side groups may be in free acid form or may be in the form of an anion and associated with a counterion, generally metal counterions, e.g. a metal selected from the alkali metals, such as lithium, sodium and potassium, alkali earth metals, such as magnesium or calcium, and transition metals, such as zinc. In some examples, the polymer having acidic sides groups can be selected from resins such as co-polymers of ethylene and an ethylenically unsaturated acid of either acrylic acid or methacrylic acid; and ionomers thereof, such as methacrylic acid and ethylene-acrylic or methacrylic acid co-polymers which are at least partially neutralized with metal ions (e.g. Zn, Na, Li) such as SURLYN® ionomers. In some examples, the polymer comprising acidic side groups can be a co-polymer of ethylene and an ethylenically unsaturated acid of either acrylic or methacrylic acid, where the ethylenically unsaturated acid of either acrylic or methacrylic acid constitute from 5 wt % to about 25 wt % of the co-polymer, in some examples from 10 wt % to about 20 wt % of the co-polymer.

In some examples, the resin may comprise two different polymers having acidic side groups. In some examples, the two polymers having acidic side groups may have different acidities, which may fall within the ranges mentioned above. In some examples, the resin may comprise a first polymer having acidic side groups that has an acidity of from 10 mg KOH/g to 110 mg KOH/g, in some examples 20 mg KOH/g to 110 mg KOH/g, in some examples 30 mg KOH/g to 110 mg KOH/g, in some examples 50 mg KOH/g to 110 mg KOH/g, and a second polymer having acidic side groups that has an acidity of 110 mg KOH/g to 130 mg KOH/g.

In some examples, the resin may comprise two different polymers having acidic side groups: a first polymer having acidic side groups that has a melt flow rate of about 10 g/10 minutes to about 50 g/10 minutes and an acidity of from 10 mg KOH/g to 110 mg KOH/g, in some examples 20 mg KOH/g to 110 mg KOH/g, in some examples 30 mg KOH/g to 110 mg KOH/g, in some examples 50 mg KOH/g to 110 mg KOH/g, and a second polymer having acidic side groups that has a melt flow rate of about 50 g/10 minutes to about 120 g/10 minutes and an acidity of 110 mg KOH/g to 130 mg KOH/g. In some examples, the first and second polymers may be absent of ester groups.

In some examples, the ratio of the first polymer having acidic side groups to the second polymer having acidic side groups can be from about 10:1 to about 2:1. In some examples, the ratio can be from about 6:1 to about 3:1, in some examples about 4:1.

In some examples, the resin may comprise a polymer having a melt viscosity of 15000 poise or less, in some examples a melt viscosity of 10000 poise or less, in some examples 1000 poise or less, in some examples 100 poise or less, in some examples 50 poise or less, in some examples 10 poise or less; said polymer may be a polymer having acidic side groups as described herein. The resin may comprise a first polymer having a melt viscosity of 15000 poise or more, in some examples 20000 poise or more, in some examples 50000 poise or more, in some examples 70000 poise or more; and in some examples, the resin may comprise a second polymer having a melt viscosity less than the first polymer, in some examples a melt viscosity of 15000 poise or less, in some examples a melt viscosity of 10000 poise or less, in some examples 1000 poise or less, in some examples 100 poise or less, in some examples 50 poise or less, in some examples 10 poise or less. The resin may comprise a first polymer having a melt viscosity of more than 60000 poise, in some examples from 60000 poise to 100000 poise, in some examples from 65000 poise to 85000 poise; a second polymer having a melt viscosity of from 15000 poise to 40000 poise, in some examples 20000 poise to 30000 poise, and a third polymer having a melt viscosity of 15000 poise or less, in some examples a melt viscosity of 10000 poise or less, in some examples 1000 poise or less, in some examples 100 poise or less, in some examples 50 poise or less, in some examples 10 poise or less; an example of the first polymer is Nucrel 960 (from DuPont), and example of the second polymer is Nucrel 699 (from DuPont), and an example of the third polymer is AC-5120 or AC-5180 (from Honeywell). The first, second and third polymers may be polymers having acidic side groups as described herein. The melt viscosity can be measured using a rheometer, e.g. a commercially available AR-2000 Rheometer from Thermal Analysis Instruments, using the geometry of: 25 mm steel plate-standard steel parallel plate, and finding the plate over plate rheometry isotherm at 120° C., 0.01 Hz shear rate.

If the resin comprises a single type of polymer, the polymer (excluding any other components of the electrophotographic ink composition) may have a melt viscosity of 6000 poise or more, in some examples a melt viscosity of 8000 poise or more, in some examples a melt viscosity of 10000 poise or more, in some examples a melt viscosity of 12000 poise or more. If the resin comprises a plurality of polymers all the polymers of the resin may together form a mixture (excluding any other components of the electrophotographic ink composition) that has a melt viscosity of 6000 poise or more, in some examples a melt viscosity of 8000 poise or more, in some examples a melt viscosity of 10000 poise or more, in some examples a melt viscosity of 12000 poise or more. Melt viscosity can be measured using standard techniques. The melt viscosity can be measured using a rheometer, e.g. a commercially available AR-2000 Rheometer from Thermal Analysis Instruments, using the geometry of: 25 mm steel plate-standard steel parallel plate, and finding the plate over plate rheometry isotherm at 120° C., 0.01 Hz shear rate.

The resin may comprise two different polymers having acidic side groups that are selected from co-polymers of ethylene and an ethylenically unsaturated acid of either acrylic acid or methacrylic acid; or ionomers thereof, such as methacrylic acid and ethylene-acrylic or methacrylic acid co-polymers which are at least partially neutralized with metal ions (e.g. Zn, Na, Li) such as SURLYN® ionomers. The resin may comprise (i) a first polymer that is a co-polymer of ethylene and an ethylenically unsaturated acid of either acrylic acid and methacrylic acid, wherein the ethylenically unsaturated acid of either acrylic or methacrylic acid constitutes from 8 wt % to about 16 wt % of the co-polymer, in some examples 10 wt % to 16 wt % of the co-polymer; and (ii) a second polymer that is a co-polymer of ethylene and an ethylenically unsaturated acid of either acrylic acid and methacrylic acid, wherein the ethylenically unsaturated acid of either acrylic or methacrylic acid constitutes from 12 wt % to about 30 wt % of the co-polymer, in some examples from 14 wt % to about 20 wt % of the co-polymer, in some examples from 16 wt % to about 20 wt % of the co-polymer in some examples from 17 wt % to 19 wt % of the co-polymer.

The resin may comprise a polymer having acidic side groups, as described above (which may be free of ester side groups), and a polymer having ester side groups. The polymer having ester side groups may be a thermoplastic polymer. The polymer having ester side groups may further comprise acidic side groups. The polymer having ester side groups may be a co-polymer of a monomer having ester side groups and a monomer having acidic side groups. The polymer may be a co-polymer of a monomer having ester side groups, a monomer having acidic side groups, and a monomer absent of any acidic and ester side groups. The monomer having ester side groups may be a monomer selected from esterified acrylic acid or esterified methacrylic acid. The monomer having acidic side groups may be a monomer selected from acrylic or methacrylic acid. The monomer absent of any acidic and ester side groups may be an alkylene monomer, including ethylene or propylene. The esterified acrylic acid or esterified methacrylic acid may, respectively, be an alkyl ester of acrylic acid or an alkyl ester of methacrylic acid. The alkyl group in the alkyl ester of acrylic or methacrylic acid may be an alkyl group having 1 to 30 carbons, in some examples 1 to 20 carbons, in some examples 1 to 10 carbons; in some examples selected from methyl, ethyl, iso-propyl, n-propyl, t-butyl, iso-butyl, n-butyl and pentyl.

In some examples, the polymer having ester side groups may be a co-polymer of a first monomer having ester side groups, a second monomer having acidic side groups and a third monomer which is an alkylene monomer absent of any acidic and ester side groups. In some examples, the polymer having ester side groups may be a co-polymer of (i) a first monomer having ester side groups selected from esterified acrylic acid or esterified methacrylic acid, in some examples an alkyl ester of acrylic or methacrylic acid, (ii) a second monomer having acidic side groups selected from acrylic or methacrylic acid and (iii) a third monomer which is an alkylene monomer selected from ethylene and propylene. In some examples, the first monomer may constitute 1% to 50% by weight of the co-polymer, in some examples 5% to 40% by weight, in some examples 5% to 20% by weight of the co-polymer, in some examples 5% to 15% by weight of the co-polymer. In some examples, the second monomer may constitute 1% to 50% by weight of the co-polymer, in some examples 5% to 40% by weight of the co-polymer, in some examples 5% to 20% by weight of the co-polymer, in some examples 5% to 15% by weight of the co-polymer. In some examples, the first monomer may constitute 5% to 40% by weight of the co-polymer, the second monomer constitutes 5% to 40% by weight of the co-polymer, and with the third monomer constituting the remaining weight of the co-polymer. In some examples, the first monomer constitutes 5% to 15% by weight of the co-polymer, the second monomer constitutes 5% to 15% by weight of the co-polymer, with the third monomer constituting the remaining weight of the co-polymer. In some examples, the first monomer constitutes 8% to 12% by weight of the co-polymer, the second monomer constitutes 8% to 12% by weight of the co-polymer, with the third monomer constituting the remaining weight of the co-polymer. In some examples, the first monomer constitutes about 10% by weight of the co-polymer, the second monomer constitutes about 10% by weight of the co-polymer, and with the third monomer constituting the remaining weight of the co-polymer. The polymer may be selected from the Bynel® class of monomer, including Bynel 2022 and Bynel 2002, which are available from DuPont®.

In some examples, the polymer having ester side groups may constitute 1% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in the liquid electrophotographic ink composition and/or the ink printed on the print substrate, e.g. the total amount of the polymer or polymers having acidic side groups and polymer having ester side groups. In some examples, the polymer having ester side groups may constitute 5% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in some examples 8% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in some examples 10% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in some examples 15% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in some examples 20% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in some examples 25% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in some examples 30% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in some examples 35% or more by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in the liquid electrophotographic composition and/or the ink printed on the print substrate. In some examples, thr polymer having ester side groups may constitute from 5% to 50% by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in the liquid electrophotographic composition and/or the ink printed on the print substrate, in some examples 10% to 40% by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in the liquid electrophotographic composition and/or the ink composition printed on the print substrate, in some examples 5% to 30% by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in the liquid electrophotographic composition and/or the ink composition printed on the print substrate, in some examples 5% to 15% by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in the liquid electrophotographic composition and/or the ink composition printed on the print substrate in some examples 15% to 30% by weight of the total amount of the resin polymers, e.g. thermoplastic resin polymers, in the liquid electrophotographic composition and/or the ink composition printed on the print substrate.

In some examples, the polymer having ester side groups may have an acidity of 50 mg KOH/g or more, in some examples an acidity of 60 mg KOH/g or more, in some examples an acidity of 70 mg KOH/g or more, in some examples an acidity of 80 mg KOH/g or more. In some examples, the polymer having ester side groups may have an acidity of 100 mg KOH/g or less, in some examples 90 mg KOH/g or less. In some examples, the polymer having ester side groups may have an acidity of 60 mg KOH/g to 90 mg KOH/g, in some examples 70 mg KOH/g to 80 mg KOH/g.

The polymer having ester side groups may have a melt flow rate of about 10 g/10 minutes to about 120 g/10 minutes, in some examples about 10 g/10 minutes to about 50 g/10 minutes, in some examples about 20 g/10 minutes to about 40 g/10 minutes, in some examples about 25 g/10 minutes to about 35 g/10 minutes.

In some examples, the resin comprises a low-melting polymer. The term “low-melting polymer” is to be understood as a polymeric material which is solid at room temperature but melts at a temperature obtainable in a printing or laminating apparatus.

In some examples, the resin may comprise a low-melting polymer with a melting point of less than about 200° C., for example less than about 190° C., for example less than about 180° C., for example less than about 170° C., for example less than about 160° C., for example less than about 150° C., for example less than about 140° C., for example less than about 130° C., for example less than about 120° C., for example less than about 110° C., for example less than about 100° C., for example less than about 80° C., for example about 70° C.

In some examples, the resin may comprise a low-melting polymer with a melting point of greater than about 80° C., for example greater than about 90° C., for example greater than about 100° C., for example greater than about 110° C., for example greater than about 120° C., for example greater than about 130° C., for example greater than about 140° C., for example greater than about 150° C., for example greater than about 160° C., for example greater than about 170° C., for example greater than about 180° C., for example greater than about 190° C., for example about 200° C.

In some examples, the resin may comprise a low-melting polymer with a melting point in the range of from about 80° C. to about 120° C.

In some examples, the melting point of the resin may be the melting point measured according to ASTM D3418.

The polymer, polymers, co-polymer or co-polymers of the resin can in some examples be selected from the Nucrel family of toners (e.g. Nucrel 403™, Nucrel 407™, Nucrel 609HS™, Nucrel 908HS™, Nucrel 1202HC™, Nucrel 30707™, Nucrel 1214™, Nucrel 903™, Nucrel 3990™, Nucrel 910™, Nucrel 925™, Nucrel 699™, Nucrel 599™, Nucrel 960™, Nucrel RX 76™, Nucrel 2806™, Bynell 2002, Bynell 2014, Bynell 2020 and Bynell 2022, (sold by E. I. du PONT)), the AC family of toners (e.g. AC-5120, AC-5180, AC-540, AC-580 (sold by Honeywell)), the Aclyn family of toners (e.g. Aclyn 201, Aclyn 246, Aclyn 285, and Aclyn 295), and the Lotader family of toners (e.g. Lotader 2210, Lotader, 3430, and Lotader 8200 (sold by Arkema)).

The resin can constitute about 5 to 90%, in some examples about 50 to 80%, by weight of the solids of the liquid electrophotographic composition and/or the ink composition printed on the print substrate. The resin can constitute about 60 to 95%, in some examples about 70 to 95%, by weight of the solids of the liquid electrophotographic composition and/or the ink composition printed on the print substrate.

Carrier Liquid

In some examples, the electrostatic ink composition comprises resin coated pigment particles, or resin particles, which are formed in and/or dispersed in a carrier fluid or carrier liquid. Before application to the print substrate in the electrostatic printing process, the composition may be an electrostatic ink composition, which may be in dry form, for example in the form of flowable pigment particles coated with the thermoplastic resin. In some examples, before application to the print substrate in the electrostatic printing process, the electrostatic ink composition may be in liquid form; and may comprise a carrier liquid in which is suspended pigment particles coated with the thermoplastic resin.

Generally, the carrier liquid acts as a reaction solvent in preparing the coated pigment particles, and can also act as a dispersing medium for the other components in the resulting electrostatic ink composition. In some examples, the carrier liquid is a liquid which does not dissolve the polymer resin at room temperature. In some examples, the carrier liquid is a liquid which dissolves the polymer resin at elevated temperatures. For example, the polymer resin may be soluble in the carrier liquid when heated to a temperature of at least 80° C., for example 90° C., for example 100° C., for example 110° C., for example 120° C. For example, the carrier liquid can comprise or be a hydrocarbon, silicone oil, vegetable oil, etc. In some examples, the carrier liquid can include an insulating, non-polar, non-aqueous liquid that can be used as a medium for toner particles. The carrier liquid can include compounds that have a resistivity in excess of about 10⁹ ohm-cm. The carrier liquid may have a dielectric constant below about 5, in some examples below about 3. The carrier liquid can include hydrocarbons. The hydrocarbon can include an aliphatic hydrocarbon, an isomerized aliphatic hydrocarbon, branched chain aliphatic hydrocarbons, aromatic hydrocarbons, and combinations thereof. Examples of the carrier liquids include aliphatic hydrocarbons, isoparaffinic compounds, paraffinic compounds, dearomatized hydrocarbon compounds, and the like. In particular, the carrier liquids can include Isopar-G™, Isopar-H™, Isopar-L™, Isopar-M™, Isopar-K™, Isopar-V™, Norpar 12™, Norpar 13™, Norpar 15™, Exxol D40™, Exxol D80™, Exxol D100™, Exxol D130™, and Exxol D140™ (each sold by EXXON CORPORATION); Teclen N-16™, Teclen N-20™, Teclen N-22™, Nisseki Naphthesol L™, Nisseki Naphthesol M™, Nisseki Naphthesol H™, #0 Solvent L™, #0 Solvent M™, #0 Solvent H™, Nisseki Isosol 300™, Nisseki Isosol 400™, AF-4™, AF-5™, AF-6™ and AF-7™ (each sold by NIPPON OIL CORPORATION); IP Solvent 1620™ and IP Solvent 2028™ (each sold by IDEMITSU PETROCHEMICAL CO., LTD.); Amsco OMS™ and Amsco 460™ (each sold by AMERICAN MINERAL SPIRITS CORP.); and Electron, Positron, New II, Purogen HF (100% synthetic terpenes) (sold by ECOLINK™).

Before printing, the carrier liquid can constitute about 20% to 99.5% by weight of the electrostatic ink composition, in some examples 50% to 99.5% by weight of the electrostatic ink composition. Before printing, the carrier liquid may constitute about 40 to 90% by weight of the electrostatic ink composition. Before printing, the carrier liquid may constitute about 60% to 80% by weight of the electrostatic ink composition. Before printing, the carrier liquid may constitute about 90% to 99.5% by weight of the electrostatic ink composition, in some examples 95% to 99% by weight of the electrostatic ink composition.

The electrostatic ink composition, when printed on the print substrate, may be substantially free from carrier liquid. In an electrostatic printing process and/or afterwards, the carrier liquid may be removed, e.g. by an electrophoresis processes during printing and/or evaporation, such that substantially just solids are transferred to the print substrate. Substantially free from carrier liquid may indicate that the ink printed on the print substrate contains less than 5 wt % carrier liquid, in some examples, less than 2 wt % carrier liquid, in some examples less than 1 wt % carrier liquid, in some examples less than 0.5 wt % carrier liquid. In some examples, the ink printed on the print substrate is free from carrier liquid.

Charge Director and Charge Adjuvant

The liquid electrophotographic composition and/or the ink composition printed on the print substrate can comprise a charge director. A charge director can be added to an electrostatic composition to impart a charge of a desired polarity and/or maintain sufficient electrostatic charge on the particles of an electrostatic ink composition. The charge director may comprise ionic compounds, including metal salts of fatty acids, metal salts of sulfo-succinates, metal salts of oxyphosphates, metal salts of alkyl-benzenesulfonic acid, metal salts of aromatic carboxylic acids or sulfonic acids, as well as zwitterionic and non-ionic compounds, such as polyoxyethylated alkylamines, lecithin, polyvinylpyrrolidone, organic acid esters of polyvalent alcohols, etc. The charge director may be selected from oil-soluble petroleum sulfonates (e.g. neutral Calcium Petronate™, neutral Barium Petronate™, and basic Barium Petronate™) polybutylene succinimides (e.g. OLOA™ 1200 and Amoco 575), and glyceride salts (e.g. sodium salts of phosphated mono- and diglycerides with unsaturated and saturated acid substituents), sulfonic acid salts including barium, sodium, calcium, and aluminium salts of sulfonic acid. The sulfonic acids may include alkyl sulfonic acids, aryl sulfonic acids, and sulfonic acids of alkyl succinates (e.g. see WO 2007/130069). The charge director can impart a negative charge or a positive charge on the resin-containing particles of an electrostatic ink composition.

The charge director can comprise a sulfosuccinate moiety of the general formula: [R_(a)—O—C(O)CH₂CH(SO₃ ⁻)C(O)—O—R_(b)], where each of R_(a) and R_(b) is an alkyl group. In some examples, the charge director comprises nanoparticles of a simple salt and a sulfosuccinate salt of the general formula MA_(n), wherein M is a metal, n is the valence of M, and A is an ion of the general formula [R_(a)—O—C(O)CH₂CH(SO₃ ⁻)C(O)—O—R_(b)], where each of R_(a) and R_(b) is an alkyl group, or other charge directors as found in WO2007130069, which is incorporation herein by reference in its entirety. As described in WO2007130069, the sulfosuccinate salt of the general formula MA_(n) is an example of a micelle forming salt. The charge director may be substantially free or free of an acid of the general formula HA, where A is as described above. The charge director may comprise micelles of said sulfosuccinate salt enclosing at least some of the nanoparticles. The charge director may comprise at least some nanoparticles having a size of 200 nm or less, in some examples 2 nm or more. As described in WO2007130069, simple salts are salts that do not form micelles by themselves, although they may form a core for micelles with a micelle forming salt. The ions constructing the simple salts are all hydrophilic. The simple salt may comprise a cation selected from Mg, Ca, Ba, NH₄, tert-butyl ammonium, Li⁺, and Al⁺³, or from any sub-group thereof. The simple salt may comprise an anion selected from SO₄ ²⁻, PO³⁻, NO₃ ⁻, HPO₄ ²⁻, CO₃ ²⁻, acetate, trifluoroacetate (TFA), Cl⁻, Bf, F⁻, ClO₄ ⁻, and TiO₃ ⁴⁻, or from any sub-group thereof. The simple salt may be selected from CaCO₃, Ba₂TiO₃, Al₂(SO₄), A1(NO₃)₃, Ca₃(PO₄)₂, BaSO₄, BaHPO₄, Ba₂(PO₄)₃, CaSO₄, (NH₄)₂CO₃, (NH₄)₂SO₄, NH₄OAc, Tert-butyl ammonium bromide, NH₄NO₃, LiTFA, Al₂(SO₄)₃, LiClO₄ and LiBF₄, or any sub-group thereof. The charge director may further comprise basic barium petronate (BBP).

In the formula [R_(a)—O—C(O)CH₂CH(SO₃ ⁻)C(O)—O—R_(b)], in some examples, each of R_(a) and R_(b) is an aliphatic alkyl group. In some examples, each of R_(a) and R_(b) independently is a C₆₋₂₅ alkyl. In some examples, said aliphatic alkyl group is linear. In some examples, said aliphatic alkyl group is branched. In some examples, said aliphatic alkyl group includes a linear chain of more than 6 carbon atoms. In some examples, R_(a) and R_(b) are the same. In some examples, at least one of R_(a) and R_(b) is C₁₃H₂₇. In some examples, M is Na, K, Cs, Ca, or Ba. The formula [R_(a)—O—C(O)CH₂CH(SO₃ ⁻)C(O)—O—R_(b)] and/or the formula MA_(n) may be as defined in any part of WO2007130069.

The charge director may comprise (i) soya lecithin, (ii) a barium sulfonate salt, such as basic barium petronate (BPP), and (iii) an isopropyl amine sulfonate salt. Basic barium petronate is a barium sulfonate salt of a 21-26 hydrocarbon alkyl, and can be obtained, for example, from Chemtura. An example isopropyl amine sulphonate salt is dodecyl benzene sulfonic acid isopropyl amine, which is available from Croda.

In an electrostatic ink composition, the charge director can constitute about 0.001% to 20%, in some examples 0.01 to 20% by weight, in some examples 0.01 to 10% by weight, in some examples 0.01 to 1% by weight of the solids of the electrostatic ink composition and/or ink composition printed on the print substrate. The charge director can constitute about 0.001 to 0.15% by weight of the solids of the liquid electrophotographic ink composition and/or ink composition printed on the print substrate, in some examples 0.001 to 0.15%, in some examples 0.001 to 0.02% by weight of the solids of the liquid electrophotographic ink composition and/or ink composition printed on the print substrate. In some examples, the charge director imparts a negative charge on the electrostatic ink composition. The particle conductivity may range from 50 to 500 pmho/cm, in some examples from 200-350 pmho/cm.

The liquid electrophotographic ink composition and/or ink composition printed on the print substrate can include a charge adjuvant. A charge adjuvant may be present with a charge director, and may be different to the charge director, and act to increase and/or stabilise the charge on particles, e.g. resin-containing particles, of an electrostatic composition. The charge adjuvant can include barium petronate, calcium petronate, Co salts of naphthenic acid, Ca salts of naphthenic acid, Cu salts of naphthenic acid, Mn salts of naphthenic acid, Ni salts of naphthenic acid, Zn salts of naphthenic acid, Fe salts of naphthenic acid, Ba salts of stearic acid, Co salts of stearic acid, Pb salts of stearic acid, Zn salts of stearic acid, Al salts of stearic acid, Cu salts of stearic acid, Fe salts of stearic acid, metal carboxylates (e.g. Al tristearate, Al octanoate, Li heptanoate, Fe stearate, Fe distearate, Ba stearate, Cr stearate, Mg octanoate, Ca stearate, Fe naphthenate, Zn naphthenate, Mn heptanoate, Zn heptanoate, Ba octanoate, Al octanoate, Co octanoate, Mn octanoate, and Zn octanoate), Co lineolates, Mn lineolates, Pb lineolates, Zn lineolates, Ca oleates, Co oleates, Zn palmirate, Ca resinates, Co resinates, Mn resinates, Pb resinates, Zn resinates, AB diblock co-polymers of 2-ethylhexyl methacrylate-co-methacrylic acid calcium, and ammonium salts, co-polymers of an alkyl acrylamidoglycolate alkyl ether (e.g. methyl acrylamidoglycolate methyl ether-co-vinyl acetate), and hydroxy bis(3,5-di-tert-butyl salicylic) aluminate monohydrate. In some examples, the charge adjuvant is aluminium di and/or tristearate and/or aluminium di and/or tripalmitate.

The charge adjuvant can constitute about 0.1 to 5% by weight of the solids of the liquid electrophotographic ink composition and/or ink composition printed on the print substrate. The charge adjuvant can constitute about 0.5 to 4% by weight of the solids of the liquid electrophotographic ink composition and/or ink composition printed on the print substrate. The charge adjuvant can constitute about 1 to 3% by weight of the solids of the liquid electrophotographic ink composition and/or ink composition printed on the print substrate.

Other Additives

The electrostatic ink composition may include an additive or a plurality of additives. The additive or plurality of additives may be added at any stage of the method. The additive or plurality of additives may be selected from a wax, a surfactant, biocides, organic solvents, viscosity modifiers, materials for pH adjustment, sequestering agents, preservatives, compatibility additives, emulsifiers and the like. The wax may be an incompatible wax. As used herein, “incompatible wax” may refer to a wax that is incompatible with the resin. Specifically, the wax phase separates from the resin phase upon the cooling of the resin fused mixture on a print substrate during and after the transfer of the ink film to the print substrate, e.g. from an intermediate transfer member, which may be a heated blanket.

Sealant Layer

In some examples, the flexible packaging material comprises a sealant layer disposed on a second surface of the base material. The second surface being a surface other than the surface on which the electrostatic ink composition is printed, for example, the second surface of the base material may be a surface opposing the first surface of the base material. In this example, the sealant layer is disposed on the innermost surface of the flexible packaging material and serves to provide means for sealing the flexible packaging material to itself or another material, with the goods to be packaged inside. In some examples the sealant layer comprises a film of low-melting, i.e. heat sealable, thermoplastic material. Suitable thermoplastic materials include those described herein in connection with the polymer resin and/or the thermally activatable laminating material and include polymers of ethylene, or DuPont's SURLYN® ionomers. In some examples, the sealant layer comprises an extrudable material.

In some examples, the sealant layer comprises a thin film of a polymer, wherein the film is less than 100 μm in thickness, for example less than 90 μm in thickness, less than 80 μm in thickness, less than 70 μm in thickness, less than 60 μm in thickness, less than 50 μm in thickness, less than 40 μm in thickness, less than 30 μm in thickness, less than 20 μm in thickness, less than 15 μm in thickness. In some examples, the film of polymer is about 12 μm in thickness.

In some examples, the sealant layer comprises a thin film of a polymer, wherein the film is greater than 12 μm in thickness, for example greater than 15 μm in thickness, greater than 20 μm in thickness, greater than 30 μm in thickness, greater than 40 μm in thickness, greater than 50 μm in thickness, greater than 60 μm in thickness, greater than 70 μm in thickness, greater than 80 μm in thickness, greater than 90 μm in thickness. In some examples, the film of polymer is about 100 μm in thickness.

Flexible Substrate

Since the flexible substrate forms the outermost layer of the final, laminated flexible packaging material as prepared in the methods described herein, in some examples the flexible substrate is transparent in order that the printed image or information on the first surface of the base material is visible to the consumer.

In some examples, the flexible substrate comprises a film of a polymer, for example a thermoplastic polymer. In some examples, the flexible substrate comprises a film of biaxially oriented polypropylene (BOPP), polyethylene terephthalate (PET), or oriented polyamide (OPA).

In some examples, the flexible substrate comprises a thin film of a polymer, wherein the film is less than 100 μm in thickness, for example less than 90 μm in thickness, less than 80 μm in thickness, less than 70 μm in thickness, less than 60 μm in thickness, less than 50 μm in thickness, less than 40 μm in thickness, less than 30 μm in thickness, less than 20 μm in thickness, less than 15 μm in thickness. In some examples, the film of polymer is about 12 μm in thickness.

In some example, the flexible substrate comprises a thin film of a polymer, wherein the film is greater than 12 μm in thickness, for example greater than 15 μm in thickness, greater than 20 μm in thickness, greater than 30 μm in thickness, greater than 40 μm in thickness, greater than 50 μm in thickness, greater than 60 μm in thickness, greater than 70 μm in thickness, greater than 80 μm in thickness, greater than 90 μm in thickness. In some examples, the film of polymer is about 100 μm in thickness.

In some examples, the flexible substrate has a first surface on which a thermally activatable laminating layer is deposited, with a second surface of the flexible substrate forming the outermost surface of the flexible packaging material. The second surface of the flexible substrate being a surface other than the surface on which the thermally activatable laminating layer is deposited, for example, the second surface of the flexible substrate may be a surface opposing the first surface of the flexible substrate. In this way, the printed image or information on the first surface of the base material is embedded within the multi-layer structure of the flexible packaging material and not on the outermost surface when the thermally activatable laminating layer disposed on the flexible substrate is contacted with the printed base material, and thus protected from damage when the base material is laminated to the flexible substrate.

Thermally Activatable Laminating Layer

The flexible packaging material and the processes for preparing the flexible packaging material comprise a thermally activatable laminating layer, also referred to as a thermal laminating material or layer or thermally activatable laminating material.

In some examples, the thermally activatable laminating layer comprises a polymer resin, for example a thermoplastic polymer resin. In some examples the thermally activatable laminating layer comprises a low-melting polymer. The term “low-melting polymer” is to be understood as a polymeric material which is solid at room temperature but melts at a temperature obtainable in a printing or laminating apparatus.

In some examples, the thermally activatable laminating layer or material may comprise a low-melting polymer with a melting point of less than about 250° C., for example less than about 220° C., for example less than about 190° C., for example less than about 180° C., for example less than about 170° C., for example less than about 160° C., for example less than about 150° C., for example less than about 140° C., for example less than about 130° C., for example less than about 120° C., for example less than about 110° C., for example less than about 100° C., for example less than about 80° C., for example less than about 70° C., for example less than about 60° C.

In some examples, the thermally activatable laminating layer or material may comprise a low-melting polymer with a melting point of greater than about 60° C., for example greater than about 70° C., for example greater than about 80° C., for example greater than about 90° C., for example greater than about 100° C., for example greater than about 110° C., for example greater than about 120° C., for example greater than about 130° C., for example greater than about 140° C., for example greater than about 150° C., for example greater than about 160° C., for example greater than about 170° C., for example greater than about 180° C., for example greater than about 190° C., for example great than about 200° C., for example great than about 220° C., for example great than about 250° C.

In some examples, the thermally activatable laminating layer or material may comprise a low-melting polymer with a melting point in the range of from about 60° C. to about 120° C.

In some examples, the melting point of a low melting polymer may be the melting point measured according to ASTM D3418.

By using a low-melting polymer as the thermally activatable laminating material to form the thermally activatable laminating layer, it becomes possible to extrude the thermally activatable laminating material onto the base material to form a layered structure for laminating to the printed substrate.

In some examples, the thermally activatable laminating layer comprises a thin film of a polymer, wherein the film is less than 100 μm in thickness, for example less than 80 μm in thickness, less than 60 μm in thickness, less than 50 μm in thickness, less than 40 μm in thickness, less than 30 μm in thickness, less than 20 μm in thickness, less than 10 μm in thickness, less than 9 μm in thickness, less than 8 μm in thickness, less than 7 μm in thickness, less than 6 μm in thickness, less than 5 μm in thickness, less than 4 μm in thickness, less than 3 μm in thickness. In some examples, the film of polymer is about 2 μm in thickness.

In some examples, the thermally activatable laminating layer or material comprises a thin film of a polymer, wherein the film is greater than 2 μm in thickness, for example greater than 3 μm in thickness, greater than 4 μm in thickness, greater than 5 μm in thickness, greater than 6 μm in thickness, greater than 7 μm in thickness, greater than 8 μm in thickness, greater than 9 μm in thickness, greater than 10 μm in thickness, greater than 20 μm in thickness, greater than 30 μm in thickness, greater than 40 μm in thickness, greater than 50 μm in thickness, greater than 60 μm in thickness, greater than 80 μm in thickness, greater than 100 μm in thickness. In some examples, the film of polymer is about 100 μm in thickness.

In some examples, the thermally activatable laminating layer comprises a thin film of a polymer, wherein the film has a coating weight of less than 50 grams per square metre (gsm), for example less than 40 gsm for example less than 30 gsm for example less than 20 gsm for example less than 15 gsm for example less than 10 gsm for example less than 9 gsm for example less than 9 gsm, less than 8 gsm, less than 7 gsm, less than 6 gsm, less than 5 gsm, less than 4 gsm, less than 3 gsm. In some examples, the weight of the film of polymer is about 2 gsm.

In some examples, the thermally activatable laminating layer comprises a thin film of a polymer, wherein the film is greater than 2 gsm in weight, for example greater than 3 gsm, greater than 4 gsm, greater than 5 gsm, greater than 6 gsm, greater than 7 gsm, greater than 8 gsm, greater than 9 gsm, greater than 10 gsm, greater than 15 gsm, greater than 20 gsm, greater than 30 gsm, greater than 40 gsm. In some examples, the weight of the film of polymer is about 50 gsm.

In some examples, the polymer may be selected from ethylene or propylene acrylic acid co-polymers; ethylene or propylene methacrylic acid co-polymers; ethylene vinyl acetate co-polymers; co-polymers of ethylene or propylene (e.g. 80 wt % to 99.9 wt %), and alkyl (e.g. C1 to C5) ester of methacrylic or acrylic acid (e.g. 0.1 wt % to 20 wt %); co-polymers of ethylene (e.g. 80 wt % to 99.9 wt %), acrylic or methacrylic acid (e.g. 0.1 wt % to 20.0 wt %) and alkyl (e.g. C1 to C5) ester of methacrylic or acrylic acid (e.g. 0.1 wt % to 20 wt %); co-polymers of ethylene or propylene (e.g. 70 wt % to 99.9 wt %) and maleic anhydride (e.g. 0.1 wt % to 30 wt %); polyethylene; polystyrene; isotactic polypropylene (crystalline); co-polymers of ethylene ethylene ethyl acrylate; polyesters; polyvinyl toluene; polyamides; styrene/butadiene co-polymers; epoxy resins; acrylic resins (e.g. co-polymer of acrylic or methacrylic acid and at least one alkyl ester of acrylic or methacrylic acid wherein alkyl may have from 1 to about 20 carbon atoms, such as methyl methacrylate (e.g. 50% to 90%)/methacrylic acid (e.g. 0 wt % to 20 wt %)/ethylhexylacrylate (e.g. 10 wt % to 50 wt %)); ethylene-acrylate terpolymers:ethylene-acrylic esters-maleic anhydride (MAH) or glycidyl methacrylate (GMA) terpolymers; ethylene-acrylic acid ionomers, urethane polymers and combinations thereof.

The thermally activatable laminating layer or material may comprise a polymer having acidic side groups. Examples of the polymer having acidic side groups will now be described. The polymer having acidic side groups may have an acidity of 50 mg KOH/g or more, in some examples an acidity of 60 mg KOH/g or more, in some examples an acidity of 70 mg KOH/g or more, in some examples an acidity of 80 mg KOH/g or more, in some examples an acidity of 90 mg KOH/g or more, in some examples an acidity of 100 mg KOH/g or more, in some examples an acidity of 105 mg KOH/g or more, in some examples 110 mg KOH/g or more, in some examples 115 mg KOH/g or more. The polymer having acidic side groups may have an acidity of 200 mg KOH/g or less, in some examples 190 mg or less, in some examples 180 mg or less, in some examples 130 mg KOH/g or less, in some examples 120 mg KOH/g or less. Acidity of a polymer, as measured in mg KOH/g can be measured using standard procedures, for example using the procedure described in ASTM D1386.

The thermally activatable laminating layer or material may comprise a polymer, in some examples a polymer having acidic side groups, that has a melt flow rate of less than about 70 g/10 minutes, in some examples about 60 g/10 minutes or less, in some examples about 50 g/10 minutes or less, in some examples about 40 g/10 minutes or less, in some examples 30 g/10 minutes or less, in some examples 20 g/10 minutes or less, in some examples 10 g/10 minutes or less. In some examples, all polymers having acidic side groups and/or ester groups in the particles each individually have a melt flow rate of less than 90 g/10 minutes, 80 g/10 minutes or less, in some examples 80 g/10 minutes or less, in some examples 70 g/10 minutes or less, in some examples 70 g/10 minutes or less, in some examples 60 g/10 minutes or less.

The polymer having acidic side groups can have a melt flow rate of about 10 g/10 minutes to about 120 g/10 minutes, in some examples about 10 g/10 minutes to about 70 g/10 minutes, in some examples about 10 g/10 minutes to 40 g/10 minutes, in some examples 20 g/10 minutes to 30 g/10 minutes. The polymer having acidic side groups can have a melt flow rate of, in some examples, about 50 g/10 minutes to about 120 g/10 minutes, in some examples 60 g/10 minutes to about 100 g/10 minutes. The melt flow rate can be measured using standard procedures, for example as described in ASTM D1238.

The acidic side groups may be in free acid form or may be in the form of an anion and associated with a counterion, e.g. metal counterions, e.g. a metal selected from the alkali metals, such as lithium, sodium and potassium, alkali earth metals, such as magnesium or calcium, and transition metals, such as zinc. The polymer having acidic sides groups can be selected from resins such as co-polymers of ethylene and an ethylenically unsaturated acid of either acrylic acid or methacrylic acid; and ionomers thereof, such as methacrylic acid and ethylene-acrylic or methacrylic acid co-polymers which are at least partially neutralized with metal ions (e.g. Zn, Na, Li) such as SURLYN® ionomers. The polymer comprising acidic side groups can be a co-polymer of ethylene and an ethylenically unsaturated acid of either acrylic or methacrylic acid, where the ethylenically unsaturated acid of either acrylic or methacrylic acid constitute from 5 wt % to about 25 wt % of the co-polymer, in some examples from 10 wt % to about 20 wt % of the co-polymer.

The thermally activatable laminating layer or material may comprise two different polymers having acidic side groups. The two polymers having acidic side groups may have different acidities, which may fall within the ranges mentioned above. The resin may comprise a first polymer having acidic side groups that has an acidity of from 10 mg KOH/g to 110 mg KOH/g, in some examples 20 mg KOH/g to 110 mg KOH/g, in some examples 30 mg KOH/g to 110 mg KOH/g, in some examples 50 mg KOH/g to 110 mg KOH/g, and a second polymer having acidic side groups that has an acidity of 110 mg KOH/g to 130 mg KOH/g.

The thermally activatable laminating layer or material may comprise two different polymers having acidic side groups: a first polymer having acidic side groups that has a melt flow rate of about 10 g/10 minutes to about 50 g/10 minutes and an acidity of from 10 mg KOH/g to 110 mg KOH/g, in some examples 20 mg KOH/g to 110 mg KOH/g, in some examples 30 mg KOH/g to 110 mg KOH/g, in some examples 50 mg KOH/g to 110 mg KOH/g, and a second polymer having acidic side groups that has a melt flow rate of about 50 g/10 minutes to about 120 g/10 minutes and an acidity of 110 mg KOH/g to 130 mg KOH/g. The first and second polymers may be absent of ester groups.

The ratio of the first polymer having acidic side groups to the second polymer having acidic side groups can be from about 10:1 to about 2:1. The ratio can be from about 6:1 to about 3:1, in some examples about 4:1.

The thermally activatable laminating layer or material may comprise a polymer having a melt viscosity of 15000 poise or less, in some examples a melt viscosity of 10000 poise or less, in some examples 1000 poise or less, in some examples 100 poise or less, in some examples 50 poise or less, in some examples 10 poise or less; said polymer may be a polymer having acidic side groups as described herein. The resin may comprise a first polymer having a melt viscosity of 15000 poise or more, in some examples 20000 poise or more, in some examples 50000 poise or more, in some examples 70000 poise or more; and in some examples, the resin may comprise a second polymer having a melt viscosity less than the first polymer, in some examples a melt viscosity of 15000 poise or less, in some examples a melt viscosity of 10000 poise or less, in some examples 1000 poise or less, in some examples 100 poise or less, in some examples 50 poise or less, in some examples 10 poise or less. The resin may comprise a first polymer having a melt viscosity of more than 60000 poise, in some examples from 60000 poise to 100000 poise, in some examples from 65000 poise to 85000 poise; a second polymer having a melt viscosity of from 15000 poise to 40000 poise, in some examples 20000 poise to 30000 poise, and a third polymer having a melt viscosity of 15000 poise or less, in some examples a melt viscosity of 10000 poise or less, in some examples 1000 poise or less, in some examples 100 poise or less, in some examples 50 poise or less, in some examples 10 poise or less; an example of the first polymer is Nucrel 960 (from DuPont), and example of the second polymer is Nucrel 699 (from DuPont), and an example of the third polymer is AC-5120 or AC-5180 (from Honeywell). The first, second and third polymers may be polymers having acidic side groups as described herein. The melt viscosity can be measured using a rheometer, e.g. a commercially available AR-2000 Rheometer from Thermal Analysis Instruments, using the geometry of: 25 mm steel plate-standard steel parallel plate, and finding the plate over plate rheometry isotherm at 120° C., 0.01 Hz shear rate.

If the thermally activatable laminating layer or material comprises a single type of polymer, the polymer may have a melt viscosity of 6000 poise or more, in some examples a melt viscosity of 8000 poise or more, in some examples a melt viscosity of 10000 poise or more, in some examples a melt viscosity of 12000 poise or more. If the thermally activatable laminating layer or material comprises a plurality of polymers all the polymers may together form a mixture that has a melt viscosity of 6000 poise or more, in some examples a melt viscosity of 8000 poise or more, in some examples a melt viscosity of 10000 poise or more, in some examples a melt viscosity of 12000 poise or more. Melt viscosity can be measured using standard techniques. The melt viscosity can be measured using a rheometer, e.g. a commercially available AR-2000 Rheometer from Thermal Analysis Instruments, using the geometry of: 25 mm steel plate-standard steel parallel plate, and finding the plate over plate rheometry isotherm at 120° C., 0.01 Hz shear rate.

The thermally activatable laminating layer or material may comprise two different polymers having acidic side groups that are selected from co-polymers of ethylene and an ethylenically unsaturated acid of either acrylic acid or methacrylic acid; or ionomers thereof, such as methacrylic acid and ethylene-acrylic or methacrylic acid co-polymers which are at least partially neutralized with metal ions (e.g. Zn, Na, Li) such as SURLYN® ionomers. The thermally activatable laminating layer or material may comprise (i) a first polymer that is a co-polymer of ethylene and an ethylenically unsaturated acid of either acrylic acid and methacrylic acid, wherein the ethylenically unsaturated acid of either acrylic or methacrylic acid constitutes from 8 wt % to about 16 wt % of the co-polymer, in some examples 10 wt % to 16 wt % of the co-polymer; and (ii) a second polymer that is a co-polymer of ethylene and an ethylenically unsaturated acid of either acrylic acid and methacrylic acid, wherein the ethylenically unsaturated acid of either acrylic or methacrylic acid constitutes from 12 wt % to about 30 wt % of the co-polymer, in some examples from 14 wt % to about 20 wt % of the co-polymer, in some examples from 16 wt % to about 20 wt % of the co-polymer in some examples from 17 wt % to 19 wt % of the co-polymer.

The thermally activatable laminating layer or material may comprise a polymer having acidic side groups, as described above (which may be free of ester side groups), and a polymer having ester side groups. The polymer having ester side groups may be a thermoplastic polymer. The polymer having ester side groups may further comprise acidic side groups. The polymer having ester side groups may be a co-polymer of a monomer having ester side groups and a monomer having acidic side groups. The polymer may be a co-polymer of a monomer having ester side groups, a monomer having acidic side groups, and a monomer absent of any acidic and ester side groups. The monomer having ester side groups may be a monomer selected from esterified acrylic acid or esterified methacrylic acid. The monomer having acidic side groups may be a monomer selected from acrylic or methacrylic acid. The monomer absent of any acidic and ester side groups may be an alkylene monomer, including ethylene or propylene. The esterified acrylic acid or esterified methacrylic acid may, respectively, be an alkyl ester of acrylic acid or an alkyl ester of methacrylic acid. The alkyl group in the alkyl ester of acrylic or methacrylic acid may be an alkyl group having 1 to 30 carbons, in some examples 1 to 20 carbons, in some examples 1 to 10 carbons; in some examples selected from methyl, ethyl, iso-propyl, n-propyl, t-butyl, iso-butyl, n-butyl and pentyl.

The polymer having ester side groups may be a co-polymer of a first monomer having ester side groups, a second monomer having acidic side groups and a third monomer which is an alkylene monomer absent of any acidic and ester side groups. The polymer having ester side groups may be a co-polymer of (i) a first monomer having ester side groups selected from esterified acrylic acid or esterified methacrylic acid, in some examples an alkyl ester of acrylic or methacrylic acid, (ii) a second monomer having acidic side groups selected from acrylic or methacrylic acid and (iii) a third monomer which is an alkylene monomer selected from ethylene and propylene. The first monomer may constitute 1% to 50% by weight of the co-polymer, in some examples 5% to 40% by weight, in some examples 5% to 20% by weight of the co-polymer, in some examples 5% to 15% by weight of the co-polymer. The second monomer may constitute 1% to 50% by weight of the co-polymer, in some examples 5% to 40% by weight of the co-polymer, in some examples 5% to 20% by weight of the co-polymer, in some examples 5% to 15% by weight of the co-polymer. The first monomer can constitute 5% to 40% by weight of the co-polymer, the second monomer constitutes 5% to 40% by weight of the co-polymer, and with the third monomer constituting the remaining weight of the co-polymer. In some examples, the first monomer constitutes 5% to 15% by weight of the co-polymer, the second monomer constitutes 5% to 15% by weight of the co-polymer, with the third monomer constituting the remaining weight of the co-polymer. In some examples, the first monomer constitutes 8% to 12% by weight of the co-polymer, the second monomer constitutes 8% to 12% by weight of the co-polymer, with the third monomer constituting the remaining weight of the co-polymer. In some examples, the first monomer constitutes about 10% by weight of the co-polymer, the second monomer constitutes about 10% by weight of the co-polymer, and with the third monomer constituting the remaining weight of the co-polymer. The polymer may be selected from the Bynel® class of monomer, including Bynel 2022 and Bynel 2002, which are available from DuPont®.

The polymer having ester side groups may have an acidity of 50 mg KOH/g or more, in some examples an acidity of 60 mg KOH/g or more, in some examples an acidity of 70 mg KOH/g or more, in some examples an acidity of 80 mg KOH/g or more. The polymer having ester side groups may have an acidity of 100 mg KOH/g or less, in some examples 90 mg KOH/g or less. The polymer having ester side groups may have an acidity of 60 mg KOH/g to 90 mg KOH/g, in some examples 70 mg KOH/g to 80 mg KOH/g.

The polymer having ester side groups may have a melt flow rate of about 10 g/10 minutes to about 120 g/10 minutes, in some examples about 10 g/10 minutes to about 50 g/10 minutes, in some examples about 20 g/10 minutes to about 40 g/10 minutes, in some examples about 25 g/10 minutes to about 35 g/10 minutes.

The thermally activatable laminating layer or material may comprise a thermoplastic polyurethane. Thermoplastic polyurethanes are formed during a polyaddition reaction between a diisocyanate, a polyol or long-chain diol and a chain extender or short-chain diol. Suitable thermoplastic polyurethanes include the Irogran®, Avalon®, Krystalgran® and Irostic® families available from Huntsman, and the Pureseal family of polymers from Ashland.

The thermoplastic polyurethane may have a melt flow rate of about 10 g/10 minutes to about 120 g/10 minutes, in some examples about 10 g/10 minutes to about 50 g/10 minutes, in some examples about 20 g/10 minutes to about 40 g/10 minutes, in some examples about 25 g/10 minutes to about 35 g/10 minutes.

The polymer, polymers, co-polymer or co-polymers of the thermally activatable laminating material can in some examples be selected from the Nucrel family of polymers (e.g. Nucrel 403™, Nucrel 407™, Nucrel 609HS™, Nucrel 908HS™, Nucrel 1202HC™, Nucrel 30707™, Nucrel 1214™, Nucrel 903™, Nucrel 3990™, Nucrel 910™, Nucrel 925™, Nucrel 699™, Nucrel 599™, Nucrel 960™, Nucrel RX 76™, Nucrel 2806™, Bynell 2002, Bynell 2014, Bynell 2020 and Bynell 2022, (sold by E. I. du PONT)), the AC family of polymers (e.g. AC-5120, AC-5180, AC-540, AC-580 (sold by Honeywell)), the Aclyn family of polymers (e.g. Aclyn 201, Aclyn 246, Aclyn 285, and Aclyn 295), the Lotader family of polymers (e.g. Lotader 2210, Lotader, 3430, and Lotader 8200 (sold by Arkema)), the Lotryl family of polymers (e.g. Lotryl MA03, Lotryl 29MA03, Lotryl 18MA02 (sold by Arkema)), the Escor family of polymers (e.g. Escor 5020 7.5% (sold by Exxon Mobil), the Escorene family of polymers (e.g. Escorene Ultra FL00328 sold by Exxon Mobil), the Tafmer family of polymers (e.g. Tafmer MA9015 (sold by Mitsui)), the Admer family of polymers (e.g. Admer AT1955E (sold by Mitsui)), the Appeel family of polymers (e.g. Appeel 20D867 (sold by DuPont)) and the Surlyn family of polymers (e.g. Surlyn 1652, Surlyn 1857 (sold by DuPont)).

In some examples, the thermally activatable laminating layer comprises a polymer selected from an ethylene-methyl acrylate copolymer, an ethylene-acrylic ester-maleic anhydride terpolymer, an acid modified polyolefin, a maleic anhydride grafted polyethylene, an ethylene acrylate polymer, and combinations thereof.

Process for Preparing the Flexible Packaging Material

Described herein is a process for preparing a flexible packaging material comprising:

-   -   providing a base material having a first surface and a second         surface, the first surface having an electrostatic ink         composition printed thereon;     -   providing a sealant layer on the second surface of the base         material;     -   providing a flexible substrate on which a thermally activatable         laminating layer has been deposited; and         -   contacting under conditions of heat and/or pressure the             thermally activatable laminating layer disposed on the             flexible substrate with the first surface of the base             material on which the electrostatic ink composition is             printed.

Also described herein is a flexible packaging material made by the process described herein.

The processes described herein are depicted generally in FIG. 1, in which the following reference numerals are used to identify the features indicated: reference numeral “1” denotes a base material; reference numeral “2” denotes an electrophotographic ink composition; reference numeral “3” denotes a sealant layer; reference numeral “4” denotes a flexible substrate; reference numeral “5” denotes a thermally activatable laminating layer or material and reference numeral “6” denotes a flexible packaging material.

FIG. 1 depicts a process in which a base material 1 is provided having a first surface 1 a having an electrophotographic ink composition 2 printed thereon. The base material also has a second surface 1 b on which a sealant layer 3 is disposed. A flexible substrate 4 having a first surface 4 a on which a thermally activatable laminating layer 5 has been deposited is also provided. The thermally activatable laminating layer 5 is then contacted with the first surface 1 a of the base material 1 comprising a printed electrophotographic ink composition 4 to form a flexible packaging material 6.

In some examples, providing a base material having a first surface having an electrostatic ink composition printed thereon comprises providing a base material and printing a liquid electrophotographic ink composition onto a first surface of a base material. The liquid electrophotographic ink composition may be printed onto the first surface of the base material in an electrophotographic or electrostatic printing process using an electrophotographic or electrostatic printing apparatus. Examples of suitable electrophotographic or electrostatic printing equipment are the HP Indigo digital presses. In some examples, the process may comprise printing a liquid electrophotographic ink composition onto a first surface of a base material, wherein the base material has a second surface on which a sealant layer is disposed. In some examples, the sealant layer may be deposited on the second surface of the base material before the liquid electrophotographic ink composition is printed onto the first surface of the base material. In some examples, the sealant layer may be deposited on the second surface of the base material after the liquid electrophotographic ink composition is printed onto the first surface of the base material.

In some examples, providing a base material having a second surface on which a sealant layer is disposed comprises depositing a sealant material to form a sealant layer on the second surface of the material. The material used to form the sealant layer may be as described previously. Depositing the sealant material onto the base material may occur before or after a liquid electrophotographic ink composition has been printed onto the first surface of the base material. Deposition of the sealant material onto the second surface of the base material may take place by any suitable process, for example, extrusion coating, flexo coating, gravure or screen printing. In some examples, the base material and sealant layer are pre-formed as a functional substrate. Therefore, in some examples, providing a base material having a first surface printed with an electrostatic ink composition and a second surface on which a sealant layer is disposed may involve providing a base material having a second surface on which a sealant layer is disposed and the printing a liquid electrophotographic ink composition on the first surface of the base material.

In some examples, the process comprises providing a flexible substrate with a thermally activatable laminating layer deposited onto a first surface of the flexible substrate. Depositing a thermally activatable laminating layer on a first surface of the flexible substrate may comprise applying a layer of thermally activatable laminating material to the flexible substrate in such a manner that the materials form a structure, for example a film, of defined layers of different materials. In one example, the depositing comprises a coating technology selected from rotogravure, screen printing, flexographic and extrusion coating technologies.

In some examples, the process comprises providing a flexible substrate with a thermally activatable laminating layer extruded onto a first surface of the flexible substrate.

In some examples, the flexible substrate having a first surface on which a thermally activatable laminating layer is disposed may be obtained by extruding a thermally activatable laminating material onto a first surface of a flexible substrate material with a thermally activatable laminating material to form a thermally activatable laminating layer disposed on a flexible substrate. The term “extrusion”, as used herein, is to be understood as meaning melting the thermally activatable laminating material and passing it through an extrusion die onto a flexible substrate in such a manner that the materials form a structure, for example a film, of defined layers of different materials. Extruding the thermally activatable laminating material onto the flexible material to form a layered structure can be performed using any apparatus suited to extrusion processes in which one material is extruded onto a flexible substrate to form layered films. In some examples, the thermally activatable laminating material comprises a blend of materials, each component of the thermally activatable laminating material may be melt blended and then extruded to form pellets of blended thermally activatable laminating material. These pellets may then be used in an extrusion process to form a thermally activatable laminating layer disposed on a flexible substrate. In some examples, during the extrusion process, a blend of materials may be used to form the thermally activatable layer.

In some examples, the flexible substrate having a first surface on which a thermally activatable laminating layer is disposed may be obtained by co-extruding a flexible substrate material with a thermally activatable laminating material to form a thermally activatable laminating layer disposed on a first surface of a flexible substrate, or providing a second flexible material comprising a flexible substrate co-extruded with a thermally activatable laminating layer. The term “co-extrusion”, as used herein, is to be understood as meaning separately melting two or more materials and passing them through separate extrusion dies in such a manner that the materials form a structure, for example a film, of defined layers of different materials. The separately extruded materials may be delivered to a single extrusion head or die which extrudes the materials in the final form. The materials from each extruder do not mix in the final extrusion die. Instead, the material layers are combined and flow out of the die as a stacked multilayer product.

In some examples, the flexible substrate having a first surface with a thermally activatable laminating layer disposed thereon is a pre-formed layered material. In some examples, the flexible substrate having a first surface with a thermally activatable laminating layer disposed thereon can be wound onto a roll or spool and stored until lamination is carried out.

In some examples, a process for preparing a flexible packaging material comprises contacting under conditions of heat and/or pressure the thermally activatable laminating layer with the first surface of the base material comprising the printed electrophotographic ink composition, e.g. the process may comprise thermally laminating the thermally activatable laminating layer with the first surface of the base material comprising the printed electrophotographic ink composition. The result of this process is a thermally laminated flexible packaging material, which, as mentioned previously, comprises the flexible substrate as the intended outermost layer of the packaging in use, thus protecting from damage the printed image or information formed by the electrophotographic ink composition. In some examples, the base material comprising the printed image or information is brought into a particular alignment with the flexible substrate comprising the thermally activatable laminating layer before being subjected to the thermal lamination.

In some examples, contacting under conditions of heat and/or pressure the thermally activatable laminating layer with the first surface of the base material comprising the printed electrostatic ink composition produces the flexible packaging material which is ready for use immediately upon cooling to room temperature. Thus, in some examples, the processes for preparing a flexible packaging material described herein require no additional curing time, or stated differently, zero curing time. The presently described processes are therefore advantageous over existing methods for producing flexible packaging materials containing LEP printed images or information in which laminating adhesives are used. Such laminating adhesives, both “solvent-based” and “solvent-free” adhesives require curing times of at least several days, thus removing the advantage of speed that digital printing can offer.

In some examples, a process for preparing a flexible packaging material comprises contacting under conditions of heat and/or pressure the thermally activatable laminating layer with the first surface of the base material comprising the printed electrostatic ink composition, and cooling the thermally laminated flexible packaging material to room temperature, thereby obtaining a ready-to-use flexible packaging material.

In some examples, the laminaton may be carried out on any apparatus suited for performing such a task. The laminating apparatus on which thermal lamination may be carried out may comprise pre-heating rolls, heating or nip rolls, and chill or cooling rolls through which the thermally laminated multilayer material passes, to further speed up the cooling process. The lamination carried out on the nip roll may be carried out at a temperature and a pressure to partially melt the thermally activatable laminating material and/or the polymer resin of the electrophotographic ink composition printed on the flexible substrate at the laminating nip, and thereby create a bond between the materials.

In some examples, the temperature for lamination, e.g. the temperature of the laminating nip, may be less than about 170° C., for example less than about 150° C., for example less than about 120° C., for example less than about 110° C., for example less than about 100° C., for example less than about 90° C., for example about 80° C.

In some examples, the temperature for lamination, e.g. the temperature of the laminating nip, may be greater than about 60° C., for example greater than about 80° C., for example greater than about 90° C., for example greater than about 100° C., for example greater than about 110° C., for example greater than about 120° C., for example about 150° C. It will be understood that the temperature for efficient thermal lamination will depend on the nature or composition of the thermally activatable laminating material and/or the polymer resin of the electrophotographic ink composition and the associated melting temperatures.

In some examples, the pressure for lamination, e.g. the pressure for the laminating nip, may be less than about 10 bar, for example less than about 9 bar, for example less than about 8 bar, for example less than about 7 bar, for example less than about 6 bar, for example less than about 5 bar, for example less than about 4 bar, for example less than about 3 bar, for example about 2 bar.

In some examples, the pressure for lamination, e.g. the pressure for the laminating nip, may be greater than about 2 bar, for example greater than about 3 bar, for example greater than about 4 bar, for example greater than about 5 bar, for example greater than about 6 bar, for example greater than about 7 bar, for example greater than about 8 bar, for example greater than about 9 bar, for example about 10 bar. It will be understood that the temperature and pressure for efficient thermal lamination will depend on the nature or composition of the thermally activatable laminating material and the associated melting temperature.

EXAMPLES

The following illustrates examples of the methods and related aspects described herein. Thus, these are merely in place to teach how to make examples of compositions of the present disclosure. As such, a representative number of compositions and their method of manufacture are disclosed herein.

Material:

Polymers: Tafmer MA9015 is an acid modified olefin elastomer from Mitsui; Escor 5020 7.5% is an ethylene-acrylic acid copolymer available from Exxon Mobil, also available from Dupont (Surlyn 1857, or Appeel 20D867); Lotryl 29MA03 and Lotryl 18MA02 is ethylene-methacrylic acid copolymer (29% and 18% respectively) available from Arkema;

Flexible Substrate:

PET (12-50 μm thick) and BOPP (15-50 μm thick) films used as flexible substrates were commercially available films, obtainable from, for example Dupont under the Mylar® brand (PET), and Innovia Films (BOPP).

Base Material

PE films (50-100 μm thick) used as flexible base materials were commercially available films, obtainable from, for example Dunmore.

Al/PE, BOPP, PET/OPA/PE, PE, and paper were also used as base materials (2-50 μm thick).

Electrophotographic ink composition: HP Electrolnk 4.5-toner particles comprising pigment encapsulated by polymer resin blends comprising Nucrel 699 and AC-5120 (in a ratio of 4:1) were dispersed in Isopar-L™, from Exxon.

Primer: DP050 (Polyethylene imine based) obtainable from Michelman.

Example 1

A commercially 90 μm MDPE available flexible film with a sealant layer was subjected to electrophotographic printing on an HP Indigo press operating under standard conditions using the DP050 primer (0.20 μm) and ink composition described above to form the printed base material with sealant layer (printed PE).

A 7 μm layer of thermally activatable laminating material (Lotryl 29MA03 (contains ethylene-methyl acrylate copolymer), available from Arkema) was extruded onto the flexible substrate (PET 12 μm) as shown in Table 1 using a commercially available extruding apparatus to provide a multilayered material comprising a layer of thermally activatable laminating material on the flexible substrate.

The printed base material comprising the sealant layer was then subjected to a thermal laminating process. The thermally activatable layer was contacted with the base material, the printed ink layer facing the thermally activatable layer on a commercially available laminating machine operating at a laminating temperature of 120° C., a laminating pressure of 4 bar and a laminating speed of 30 m/min.

The lamination bond strength for the material produced according to Example 1 was found to be 4 N/inch according to ASTM F0904-98R08.

Other flexible packaging materials were prepared according to the general methodology described above, for the different base materials and flexible substrates described above using the thermally activatable laminating materials as set out in Table 1 below.

The laminate performance was verified at zero cure time by measuring the lamination bond strength immediately after the laminated material had cured to room temperature. Lamination bond strength was measured according to ASTM F0904-98R08 (results are shown in Table 1).

TABLE 1 Thermally activatable Lamination Bond laminating layer material Material Name Strength (N/inch) Ethylene - Methyl Acrylate LOTRYL 29MA03 4-10 copolymer Arkema Ethylene - Methyl Acrylate LOTRYL 18MA02 4-10 copolymer Arkema Ethylene - Acrylic Ester - Lotader 3430 5-10 Maleic Anhydride terpolymer Arkema Acid modified polyolefin TafmerMA9015 5-10 Mitsui Maleic Anhydride grafted Admer AT1955E 5-10 Polyethylene Mitsui Ethylene acrylate Appeel 20D867 4-8  DuPont Ethylene acrylic acid Surlyn 1857, 2-4  DuPont Ethylene acrylic acid Escor 5020 7.5%, 2-4  Exxon mobile Ethylene Vinyl Acetate Escorene 2-3  Copolymer Resin UltraFL00328 Exxon mobile

The results suggest that the thermally activatable laminating layer comprising polymers/co-polymers that melt at temperatures of about 80-120° C. melt along with the electrophotographic ink composition in the laminating nip, bond to each other, and after cooling maintain bond strength values which are acceptable for many flexible packaging applications and are comparable to values measured with standard lamination techniques.

While the materials, methods and related aspects have been described with reference to certain examples, it will be appreciated that various modifications, changes, omissions, and substitutions can be made without departing from the spirit of the disclosure. The features of any dependent claim may be combined with the features of any of the other dependent claims or any and/or any of the independent claims. 

1. A process for preparing a flexible packaging material comprising: providing a base material having a first surface and a second surface, the first surface having an electrostatic ink composition printed thereon; providing a sealant layer on the second surface of the base material; providing a flexible substrate on which a thermally activatable laminating layer has been deposited; and contacting under conditions of heat and/or pressure the thermally activatable laminating layer disposed on the flexible substrate with the first surface of the base material on which the electrostatic ink composition is printed.
 2. The process of claim 1, wherein the thermally activatable laminating layer comprises a copolymer of an alkylene monomer and a monomer selected from acrylic acid and methacrylic acid.
 3. The process of claim 1, wherein the base material comprises a metallic foil or a metallized substrate.
 4. The process of claim 1, wherein the flexible substrate comprises a film of thermoplastic material.
 5. The process of claim 1, wherein the flexible substrate is transparent.
 6. The process of claim 1, wherein the flexible substrate comprises a film of biaxially orientated polypropylene or poly(ethylene) terephthalate.
 7. The process of claim 1, wherein the thermally activatable laminating layer is contacted with the first surface of the base material on which the electrostatic ink composition is printed at a temperature in the range of about 60 to 170° C.
 8. The process of claim 1, wherein the electrostatic ink composition comprises a copolymer of an alkylene monomer and a monomer selected from acrylic acid and methacrylic acid.
 9. The process of claim 1, wherein the sealant layer is provided on the second surface of the base material before or after printing of the electrostatic ink on the base material.
 10. The process of claim 1, wherein the sealant layer is provided on the second surface of the base material after contacting the thermally activatable laminating layer disposed on the flexible substrate with the first surface of the base material on which the electrostatic ink composition is printed.
 11. A flexible packaging material comprising: a base material comprising a first surface and a second surface; an electrostatic ink composition printed on the first surface of the base material; a sealant layer disposed on the second surface of the base material; a flexible substrate; and a thermally activated laminating layer disposed between and bonded to the flexible substrate and the first surface of the base material printed with the electrostatic ink composition.
 12. A material according to claim 11, wherein the flexible substrate is transparent and comprises a thermoplastic polymer.
 13. A material according to claim 11, wherein the base material comprises a metallic foil, a metallized substrate or a paper substrate.
 14. A material according to claim 11, wherein thermally activatable laminating layer comprises a copolymer of an alkylene monomer and a monomer selected from acrylic acid and methacrylic acid.
 15. A flexible package comprising a flexible material comprising: a base material comprising a first surface and a second surface; an electrophotographic ink composition printed on the first surface of the base material; a sealant layer disposed on the second surface of the base material; a flexible substrate; and a thermally activated laminating layer disposed between and bonded to the flexible substrate and the first surface of the base material printed with the ink composition. 